Tem Observation Of Precipitate Structures In Al-Zn-Mg Alloys With Additions Of Cu/Ag
Al-Zn-Mg alloy has been known as one of the aluminum alloys with the good age-hardening ability and the high strength among commercial aluminum alloys. The mechanical property of the limited ductility, however, is required to further improvement. In this work, three alloys, which were added Cu or Ag into the Al-Zn-Mg alloy, were prepared to compare the effect of the additional elements on the aging behavior. The content of Ag and Cu were 0.2at.% and the same as, respectively. Ag or Cu added alloy showed higher maximum hardness than base alloy. The particle shape and rod shape precipitates were observed in all alloys peak-aged at 423K. According to addition of Ag or Cu, the number density of the precipitates increased higher than that of base alloy.
Al-Zn-Mg jest stopem, który można efektywnie poddawać procesowi utwardzania wydzieleniowego. Spośród różnorodnych stopów aluminium charakteryzuje się bardzo wysoką wytrzymałością mechaniczną, jednak jego ograniczona plastyczność jest cechą wymagającą poprawy. W toku prac przygotowano trzy stopy: stop bazowy Al-Zn-Mg oraz stopy zawierające dodatki Cu lub Ag, dla porównania wpływu tych dodatków na starzenie się materiału. Zawartość Ag i Cu wynosiła odpowiednio 0,2% at. Stopy z dodatkiem Ag lub Cu wykazywały większą twardość maksymalną w porównaniu ze stopem bazowym. We wszystkich stopach starzonych w temperaturze 423K obserwowano charakterystyczne wydzielenia, a ich koncentracja była odpowiednio większa dla stopów z dodatkiem Ag lub Cu.