Humidity Migration in Surface Layers of Sand Moulds During Processes of Penetration and Drying of Protective Coatings

Tytuł:
Humidity Migration in Surface Layers of Sand Moulds During Processes of Penetration and Drying of Protective Coatings
Autorzy:
Jamrozowicz, Łukasz
Zych, Jerzy
Tematy:
surface layers
sand mould
porous medium
humidity migration
protective coatings
resistance measurement
warstwy powierzchniowe
formy piaskowe
migracja wilgoci
powłoki ochronne
pomiar rezystancji
Data publikacji:
2022
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Język:
angielski
Prawa:
CC BY-NC-ND: Creative Commons Uznanie autorstwa - Użycie niekomercyjne - Bez utworów zależnych 3.0 PL
Źródło:
Archives of Foundry Engineering; 2022, 22, 4; 72--78
1897-3310
2299-2944
Dostawca treści:
Biblioteka Nauki
Artykuł
  Przejdź do źródła  Link otwiera się w nowym oknie
The results of investigations of humidity migration in near surface layers of sand mould during processes of penetration and drying of protective coatings are presented in the hereby paper. The process of the humidity exchanging between surroundings and moulding sands as porous materials, is widely described in the introduction. In addition, the humidity flow through porous materials, with dividing this process into stages in dependence of the humidity movement mechanism, is presented. Next the desorption process, it means the humidity removal from porous materials, was described. Elements of the drying process intensity as well as the water transport mechanisms at natural and artificial drying were explained. The innovative research stands for measuring resistance changes of porous media due to humidity migrations was applied in investigations. Aqueous zirconium coatings of two apparent viscosities 10s and 30s were used. Viscosity was determined by means of the Ford cup of a mesh clearance of 4mm. Coatings were deposited on cores made of the moulding sand containing sand matrix, of a mean grain size dL = 0.25 mm, and phenol-formaldehyde resin. Pairs of electrodes were placed in the core at depths: 2, 3, 4, 5, 8, 12 and 16 mm. Resistance measurements were performed in a continuous way. The course of the humidity migration process in the core surface layer after covering it by protective coating was determined during investigations. Investigations were performed in the room where the air temperature was: T = 22 oC but the air humidity was not controlled, as well as in the climatic chamber where the air temperature was: T =35 oC and humidity: H = 45%. During the research, it was shown that the process of penetration (sorption) of moisture into the moulding sand is a gradual process and that the moisture penetrates at least 16 mm into the sand. In the case of the drying (desorption) process, moisture from the near-surface layers of the moulding sand dries out much faster than moisture that has penetrated deeper into the sand.

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies