The Effect of Surface Texturing on the Frictional Resistance of Steel-Bronze Assembly in Lubricated Sliding
The experiments were carried out using a block-on-ring tester. The block samples made from bronze CuSn10P of 138 HB hardness were burnished to obtain surfaces with circular oil pockets. Rings were made from 42CrMo4 steel of hardness 40 HRC. Friction tests were conducted at a constant normal load of 900 N. Tests were carried out at increasing sliding speeds of the range 0.08 – 0.82 m/s, starting from the lowest speed. The every speed was maintained for two minutes. The tested assembly was inserted in the reservoir of mineral oil L-AN 46. It was found that the dimple presence on block surface reduced the friction coefficient substantially compared to non- extured turned surfaces. The area density of dimples smaller than 15% (particularly 4.5% and 6%) was beneficial.
Przeprowadzono badania tribologiczne w układzie rolka-klocek. Powierzchnie klocka (wycinka pierścienia) z brązu CuSn10P o twardości 138 HB zawierały sferyczne kieszenie smarowe uzyskane metodą wygniatania. Rolki wykonano ze stali 42CrMo4 o twardości 40 HRC. Badania tribologiczne przeprowadzono przy stałym obciążeniu normalnym wynoszącym 900 N i zwiększającej się prędkości ślizgania w zakresie 0,08–0,82 m/s, utrzymywanej w czasie dwóch minut. Skojarzenie trące smarowano olejem L-AN 46 znajdującym się w zbiorniku. Stwierdzono, że teksturowanie powierzchni klocka spowodowało istotne zmniejszenie oporów tarcia w porównaniu z parą cierną zawierającą gładkie powierzchnie, szczególnie przy niewielkich stopniach pokrycia wgłębieniami (4,5 i 6%).