Preparation and characterization of halogen-free flame retardant MCA core-shell microcapsules coated with melamine or acrylic acid resin

The resin melamine cyanurate (MCA) core-shell microcapsules were prepared by surface coating modification of halogen-free flame retardant MCA using melamine resin and acrylic resin as wall materials. The influence of different wall materials on the coating effect of halogen-free flame retardant MCA was studied by SEM, particle size analysis, IR, and DSC and TGA methods. The results showed that the melamine resin had a high degree of polymerization and decomposed at about 160°, which had a surface modification effect on MCA and did not affect its flame retardant performance. The surface coating rate of poly(methyl methacrylate) PMMA-MCA core-shell microcapsules was about 80%. After adding acrylic acid (AA) as the second monomer the coating effect was significantly improved and the thermal decomposition temperature of the wall material of the microcapsule was reduced.

Mikrokapsułki typu rdzeń-otoczka otrzymywano, modyfikując powierzchnię bezhalogenowego, opóźniającego palenie cyjanuranu melaminy (MCA) przy użyciu żywicy melaminowej lub akrylowej. Wpływ rodzaju użytego materiału na efekt powlekania powierzchni mikrokapsułki MCA badano metodami SEM, analizy wielkości cząstek, IR oraz DSC i TGA. Żywica melaminowa wykazywała wysoki stopień polimeryzacji i ulegała rozkładowi w temperaturze ok. 160°, co miało wpływ na efekt modyfikacji powierzchni MCA, ale nie zmieniało jego właściwości uniepalniających. Stopień powlekania powierzchni mikrokapsułki MCA typu rdzeń-otoczka żywicą (PMMA) poli(metakrylan metylu) wynosił ok. 80%. Po dodaniu kwasu akrylowego (AA) jako drugiego monomeru, efekt powlekania znacznie się poprawił, a temperatura rozkładu termicznego materiału ścianki mikrokapsułki się obniżyła.